Fracture behaviours of in situ silica nanoparticle-filled epoxy at different temperatures
来源:汤龙程副研究员个人网站 发布日期:2014-05-06
作者:H Zhang, LC Tang, Z Zhang, K Friedrich, S Sprenger
关键字:Nanosilica particles, Epoxy matrix, Fracture toughness
论文来源:期刊
具体来源:Polymer
发表时间:2008年
Fracture behaviours of nanosilica filled bisphenol-F epoxy resin were systematically investigated at ambient and higher temperatures (23 C and 80 C). Formed by a special sol–gel technique, the silica nanoparticles dispersed almost homogenously in the epoxy resin up to 15 vol.%. Stiffness, strength and toughness of epoxy are improved simultaneously. Moreover, enhancement on fracture toughness was much remarkable than that of stiffness. The fracture surfaces taken from different test conditions were observed for exploring the fracture mechanisms. A strong particle–matrix adhesion was found by fractography analysis. The radius of the local plastic deformation zone calculated by Irwin model was relative to the increment in fracture energy at both test temperatures. This result suggested that the local plastic deformation likely played a key role in toughening of epoxy.
Copyright © 2005 Polymer.cn All rights reserved
中国聚合物网 版权所有
经营性网站备案信息

京公网安备11010502032929号

工商备案公示信息

京ICP证050801号

京ICP备12003651号