Effect of Solid-state Stress Induced Reaction on Morphology and Structure of Metallocene Polyethylene
来源:邹华维教授个人网站 发布日期:2014-03-04
作者:Huawei Zou*, Yang Chen, Mei Liang, Pengbo Liu
关键字:polyolefins,properties and characterization,morphology
论文来源:期刊
具体来源:Journal of Applied Polymer Science, 2013, 130(3):1691-1699
发表时间:2013年

  Metallocene-catalyzed polyethylene (mPE) powder was prepared through a mechanochemical reactor in solid state at ambient temperature. The changes of morphology and structure of mPE were investigated by SEM, FTIR, DSC, viscosimetry, GPC, WAXD, dynamic rheometer, and high pressure capillary rheometer methods. FTIR measurement illustrated that the branching degree of mPE increased after mechanochemical reaction. Combined with the dynamic rheological analysis, it was proved that the rupture and combination of macromolecular chain undergo strong shear resulted in the formation of long chain branches. X-ray diffraction analysis showed that the crystal form of mPE transferred from rhombic to monoclinic system partly, and the crystalline degree increased slightly in the initial mechanochemical reaction period. Viscometer test results exhibited that molecular weight of mPE dropped during the mechanochemical treatment. Rheology measurement indicated that the critical shear rate of the shark-skin failure enhanced and the extruded stands exhibited smooth face for the mPE after mechanochemical treatment.

Copyright © 2005 Polymer.cn All rights reserved
中国聚合物网 版权所有
经营性网站备案信息

京公网安备11010502032929号

工商备案公示信息

京ICP证050801号

京ICP备12003651号