Electrochemical Performances of MCMB/(AC+LiFePO4) Lithium-Ion Capacitors
来源:时志强教授个人网站 发布日期:2013-12-14
作者:Lina Ping,Jiaming Zheng, Zhiqiang Shi*, Jie Qi, Chengyang Wang*
关键字:lithium-ion capacitors, mesocarbon microbeads, activated carbon, LiFePO4, Li+ pre-doping
论文来源:期刊
具体来源:Chinese Science Bulletin
发表时间:2013年
    Lithium-ion capacitors (LICs) were fabricated using mesocarbon microbeads (MCMB) as a negative electrode and a mixture of activated carbon (AC) and LiFePO4 as a positive electrode (abbreviated as LAC). The phase structure and morphology of LAC samples were characterized by X-ray diffraction (XRD) and field emission scanning electron microscopy (FESEM). The electrochemical performance of the LICs was studied using cyclic voltammetry, charge-discharge rate measurements, and cycle performance testing. A LIC with 30 wt% LiFePO4 was found to have the best electrochemical performance with a specific energy density of 69.02 W h kg?1 remaining at 4 C rate after 100 cycles. Compared with an AC-only positive electrode system, the ratio of practical capacity to theoretical calculated capacity of the LICs was enhanced from 42.22% to 56.59%. It was proved that adding LiFePO4 to AC electrodes not only increased the capacity of the positive electrode, but also improved the electrochemical performances of the whole LICs via Li+ pre-doping.
Copyright © 2005 Polymer.cn All rights reserved
中国聚合物网 版权所有
经营性网站备案信息

京公网安备11010502032929号

工商备案公示信息

京ICP证050801号

京ICP备12003651号