作者：Huang Ziheng,Zhang Jiaoru, ChengJiang, Xu Shouping,Pi Pihui,Cai Zhiqi,Wen Xiufang,Yang Zhuoru
关键字：gradient wettability surface ,
论文来源：期刊
具体来源：Applied Surface Science 卷: 259页: 142-6 DOI: 10.1016/j.apsusc.2012.07.006
发表时间：2012年
Gradient wettability surface was prepared on copper substrate via a facile alkali assistant surface oxidation technique. It was based on the control of cupric hydroxide (Cu(OH) 2) nanoribbon arrays growth from the upper part to lower part along the vertically placed copper substrate in an aqueous solution of NaOH and (NH 4) 2S 2O 8. Thus the gradient wettability functionalized Cu(OH) 2 nanoribbon arrays were directly fabricated on copper substrate by varying the immersing time of different positions along the substrate surface. By using a relative dilute NaOH solution (0.75mol/L) and (NH 4) 2S 2O 8 solution (0.03mol/L), and regulating dropping speed, the surface gradient wettability changing from the original contact angle of copper substrate (90.5deg) to surperhydrophilicity (3.0deg) was prepared. The surface fabricated on copper substrate may keep its gradient wetting property after immersed in water bath at 100degC for 10h. The water contact angle measurement (CA), Scanning electron microscopy (SEM), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS) were employed to analyze the wettability, morphologies, crystal structure, and surface chemical compositions of the Cu(OH) 2 nanoribbon arrays on copper substrate. This research is expected to be significant in providing a new strategy for the preparation of novel gradient wettability material with potential industrial applications on copper substrate.