Synthesis, Characterization and Properties of Degradable Poly(L-lactic acid)/Poly(butylene terephthalate) Copolyesters Containing 1,4-Cyclohexanedimethanol
来源:方征平教授个人网站 发布日期:2011-03-14
作者:Wang BT, Zhang Y*, Song PA, Guo ZH, Cheng J, Fang ZP
关键字:degradable aliphatic/aromatic copolyesters, poly(L-lactic acid), 1,4-cyclohexanedimethanol, copolymerization
论文来源:期刊
具体来源:J. Appl. Polym. Sci., 2011.6, 120(5): 2985-2995
发表时间:2011年

High molecular weight copolyesters based on poly(butylene terephthalate) (PBT) as rigid aromatic segments and poly(L-lactic acid) (PLLA) as degradable aliphatic segments were synthesized via polycondensation of terephthalic acid (TPA), 1,4-butanediol (BDO), 1,4-cyclohexanedimethanol (CHDM) and poly(L-lactic acid) oligomer (OLLA).Through tailoring the molar ratio of diols (BDO and CHDM), the effect of CHDM unit on the synthesis, mechanical properties and thermal stabilities as well as the degradation behaviors of the copolyesters was investigated. With the increase of CHDM content, the initial decomposition temperature (Tonset) increased from 282.5 ºC to 322.2 ºC and the tensile strength improved by nearly four times from 5.4 MPa to 19 MPa. When the CHDM was 5 %, the weight-average molecular weight of the copolyester was up to 89400 g/mol with a polydispersity of 1.96. In phosphate buffer solution the degradation rate of the copolyesters displayed a strong dependency on the temperature and CHDM composition.

Copyright © 2005 Polymer.cn All rights reserved
中国聚合物网 版权所有
经营性网站备案信息

京公网安备11010502032929号

工商备案公示信息

京ICP证050801号

京ICP备12003651号