Characterization and Degradability of the e-Caprolactone/lactide Graft Copolymers
来源:戴炜枫博士后个人网站 发布日期:2010-11-30
作者:Weifeng Dai, Jiayun Zhu, Aoyu Shangguan, Meidong Lang*
关键字:Poly(ε-caprolactone), Polylactide, Graft copolymers, Ring-opening polymerization,2-Oxepane-1,5-dione
论文来源:期刊
具体来源:European Polymer Journal. 2009, 45, 1659-1667
发表时间:2009年

The novel comb-type biodegradable graft copolymers based on ε-caprolactone and l-lactide were synthesized. Firstly, 2-oxepane-1,5-dione (OPD) was synthesized by the Baeyer–Villiger oxidation of 1,4-cyclohexanedione, and was subsequently copolymerized with ε-caprolactone (CL) to produce poly(2-oxepane-1,5-dione-co-ε-caprolactone) (POCL) catalyzed by stannous(II) 2-ethylhexanoate in toluene. Then, POCL was converted into poly(4-hydroxyl-ε-caprolactone-co-ε-caprolactone) (PHCL) using sodium borohydride as reductant. Finally, poly(4-hydroxyl-ε-caprolactone-co-ε-caprolactone)-g-poly(l-lactide) (PHCL-g-PLLA) were prepared successfully by bulk ring-opening polymerization of l-lactide using PHCL as a macro-initiator. All the copolymers have been characterized by 1H and 13C NMR, DSC, and GPC. Compared with the random copolymer of poly(CL-co-LA), the elongation is highly increased. And the thermal analysis showed that the crystallization rate of the PCL backbone in the graft copolymers was greatly reduced compared to the PCL homopolymer. The hydrolytic degradation of the copolymer was much faster in a phosphate buffer (pH = 7.4) at 37 °C, which is confirmed by the weight loss and change of intrinsic viscosity.

Copyright © 2005 Polymer.cn All rights reserved
中国聚合物网 版权所有
经营性网站备案信息

京公网安备11010502032929号

工商备案公示信息

京ICP证050801号

京ICP备12003651号