Eur. J. Inorg. Chem. 2010, 4367–4373 : Synthesis of Two-Dimensional Carbon and Carbon–Metal Nanocomposites Using a Natural Cellular Material as the Carbon Precursor
来源:汪勇教授个人网站 发布日期:2010-09-20
作者:Fengbin Li, Ling Li, Xingzhi Liao, Ling Tong, Zhiquan Chen, and Yong Wang*
关键字:Organic-inorganic hybrid composites / Carbon / Cellulose / Nanoflakes / Nanoparticles / Nanocomposites /
论文来源:期刊
具体来源:Eur. J. Inorg. Chem
发表时间:2010年
Two-dimensional carbon nanostructures, including carbon nanoflakes that are formed from the disassembly of carbon foams and carbon–metal composites, were directly synthesized using the stem pith of the rice-paper plant (SPRP) as the carbon precursor and also the synthesis template. SPRP has a foamlike porous structure. SPRP was pyrolyzed to prepare carbon foam with ultralow apparent density, and this foam was ruptured to produce carbon nanoflakes with a lateral size up to hundreds of micrometers and a thickness of approximately 100 nm. Palladium and platinum were added to the SPRP foams by wet impregnation, and the impreg- nated foams were subsequently converted into composites of metal nanoparticles and carbon in the form of foams or nanoflakes. The composites were characterized using electron microscopy, energy-dispersive spectroscopy, X-ray diffraction, and Raman spectroscopy. The metal nanoparticles were found to be highly crystalline with diameters in the range of several tens of nanometers (palladium) and several nanometers (platinum), and were uniformly distributed throughout the carbon nanoflakes. The amount of metal in the composite was tunable by changing the impregnation time and the concentration of the impregnation solution.
Copyright © 2005 Polymer.cn All rights reserved
中国聚合物网 版权所有
经营性网站备案信息

京公网安备11010502032929号

工商备案公示信息

京ICP证050801号

京ICP备12003651号