Unusual rheological behavior of liquid polybutadiene rubber/clay nanocomposite gels: The role of polymer-clay interaction, clay exfoliation, and clay orientation and disorientation
来源:王晓亮副教授个人网站 发布日期:2010-02-22
作者:Wang, X. L.; Gao, Y.; Mao, K. M.; Xue, G.; Chen, T. H.; Zhu, J. J.; Li, B. H.; Sun, P. C.; Jin, Q. H
关键字:rheology, exfoliation, orientation-disorientation, liquid rubber, organo-clay, nanocomposites
论文来源:期刊
具体来源:Macromolecules 2006, 39, 6653-6660.
发表时间:2006年

    The rheological properties of liquid polybutadiene rubber/organo-clay nanocomposite gels were investigated by rheological experiments, focusing on the effects of clay exfoliation and orientation-disorientation, as well as polymer-clay interaction and temperature. Both irreversible and reversible viscosity transitions were observed in the temperature range from 26 to 136 ?C in steady shear experiments on as-prepared and exfoliated samples. These transitions depend strongly on the end-groups, molecular weight of the liquid rubber and on the shear field. The irreversible transition is attributed to the exfoliation of the clay, and the reversible transition can be understood as a shear-induced orientation-disorientation transition of the clay sheets. Polymer-clay interaction is confirmed to be a key controlling factor of the orientation-disorientation transition, whereas the shear field plays a critical role to induce such a transition. To our knowledge, this is the first rheological observation of the in-situ exfoliation process and the shear-induced orientation-disorientation transition of layered silicate in polymer/organo-clay nanocomposites. A tentative model was suggested based on the clay exfoliation and orientation-disorientation transition, and the model is used to explain the observed unique rheological behavior.

Copyright © 2005 Polymer.cn All rights reserved
中国聚合物网 版权所有
经营性网站备案信息

京公网安备11010502032929号

工商备案公示信息

京ICP证050801号

京ICP备12003651号