[Langmuir, 2022] N-Oxide Zwitterion Functionalized Positively Charged Polyamide Composite Membranes for Nanofiltration
来源:赵军强副教授个人网站 发布日期:2023-08-08
作者:Hui Zhang, Yi Li, Junping Miao, Xinran Zhu, Jing Yang, Qinglei Zhang, Yanfu Yang, Junqiang Zhao**
关键字:N-oxide zwitterion, positively charge polyamide membrane, nanofiltration, anti-fouling, interfacial polymerization
论文来源:期刊
具体来源:Langmuir
发表时间:2022年

N-Oxide zwitterionic polyethyleneimine (ZPEI), a new kind of aqueous phase monomer synthesized by commercially branched polyethyleneimine (PEI) via oxidation reaction, was prepared for fabrication of thin-film composite (TFC) polyamide membranes via interfacial polymerization. The main factors, including the monomer concentration and immersion time of the aqueous phase and organic phase, were investigated. Compared with PEI-TFC membranes, the obtained optimal defect-free ZPEI-TFC membranes exhibited a lower roughness (3.3 ± 0.3 nm), a better surface hydrophilicity, and a smaller pore size (238 Da of MWCO). The positively charged ZPEI-TFC membranes (isoelectric point at pH 8.05) showed higher rejections toward both divalent cationic (MgCl2, 93.0%) and anionic (Na2SO4, 96.1%) salts with a water permeation flux of up to 81.0 L·m–2·h–1 at 6 bar, which surpassed currently reported membranes. More importantly, mainly owing to N-oxide zwitterion with strong hydration capability, ZPEI-TFC membranes displayed a high flux recovery ratio (97.0%) toward a model protein contaminant (bovine serum albumin), indicating good anti-fouling properties. Therefore, the novel N-oxide zwitterion functionalized positively charged nanofiltration membranes provide an alternative for water desalination and sewage reclamation.

Copyright © 2005 Polymer.cn All rights reserved
中国聚合物网 版权所有
经营性网站备案信息

京公网安备11010502032929号

工商备案公示信息

京ICP证050801号

京ICP备12003651号