Foaming behavior of polypropylene/polystyrene blends enhanced by improved interfacial compatibility
来源:余坚副研究员个人网站 发布日期:2009-11-20
作者:翟文涛, 王红英, 余坚*, 董金勇*, 何嘉松.
关键字:blends,microcellular foam,poly(propylene),polystyrene,supercritical
论文来源:期刊
具体来源:Journal of Polymer Science Part B-Polymer Physics, 2008, 46(16): 1641-1651.
发表时间:2008年

A series of polypropylene (PP)/polystyrene (PS) blends were prepared by solvent blending with PS-grafted PP copolymers (PP-g-PS) having different PS graft chain length as compatibilizers. The interfacial compatibility was significantly improved with increasing PS graft chain length until the interface was saturated at PS graft chain length being 3.29 3 103 g/mol. The blends were foamed by using pressure-
quenching process and supercritical CO2 as the blowing agent. The cell preferentially formed at compatibilized interface because of low energy barrier for nucleation. Combining with the increased interfacial area, the compatibilized interface lead to the foams with increased cell density compared to the  incompatibilized one. The increase in interfacial compatibility also decreased the escape of gas, held more gas for cell growth, and facilitated the increase in  expansion ratio of PP/PS blend foams.

Copyright © 2005 Polymer.cn All rights reserved
中国聚合物网 版权所有
经营性网站备案信息

京公网安备11010502032929号

工商备案公示信息

京ICP证050801号

京ICP备12003651号