The Effect of Nano-SiO2 Colloid on Soap-free Emulsion Polymerization of Methyl Methacrylate and Hydroxyethyl Methacrylate
来源:张发爱教授个人网站 发布日期:2009-10-22
作者:Cai-Li Yu; Jian-Shu Kang; Fa-Ai Zhang*
关键字:Soap-free emulsion polymerization, nano-SiO2 colloid, methyl methacrylate, hydrophilic monomer, polymerization rate,
论文来源:期刊
具体来源:Journal of Macromolecular Science, Part A: Pure and Applied Chemistry (2009) 46, 870–875
发表时间:2009年

Soap-free emulsion polymerization of methyl methacrylate (MMA) and hydroxyethyl methacrylate (HEMA) was carried out in the presence of colloidal nano-SiO2 particles. The effect of nano-SiO2 level on the monomer conversion, polymerization rate (Rp), and emulsion stability was investigated. The viscosity, particle size distribution of the emulsions, surface tension, and ionic conductivity of these systems were determined. Upon the introduction of the nano-SiO2 particles into this system, the Rp and monomer conversion increased and the average particle size of the P(MMA-HEMA) emulsion decreased in comparison to emulsions formed in the absence of nano-SiO2. However, the particle size distribution became broader to some degree. Scanning electron microscope observations demonstrated that the shape of these latex particles were uniformly spherical. The surface tension and ionic conductivity of the system increased significantly after polymerization, but the presence of nano-SiO2 resulted in an increase in surface tension and a decrease in ionic conductivity in comparison to the particle–free system.

Copyright © 2005 Polymer.cn All rights reserved
中国聚合物网 版权所有
经营性网站备案信息

京公网安备11010502032929号

工商备案公示信息

京ICP证050801号

京ICP备12003651号