Tunable Dielectric and Other Properties in High-Performance Sandwich-type Polyimide Film by Adjusting the Porous Structure
来源:马英一副教授个人网站 发布日期:2019-08-30
作者:Ma, Yingyi; Xu, Le; He, Zian; 等
关键字:Sandwich, Dielectric properties, porous film
论文来源:期刊
具体来源:J. Mater. Chem. C
发表时间:2019年
The preparation and performance adjustment of low-dielectric polyimide (PI) play important roles in the development and application of next-generation dielectric materials used in high-speed integrated circuits. Herein, composite polyimide films with sandwich-type porous structures were fabricated via a microemulsion method, in which the self-assembly of water droplets was involved. Decreases in the dielectric constant and water absorption and increases in the tensile strength and tensile modulus were simultaneously realized due to the presence of symmetrical porousstructures and a dense PI layer upon the introduction of the sandwich-type porous structure. The dielectric, mechanical and water resistance properties of the composite PI films could be further regulated by controlling the porous structure using different conditions for film formation. Byvarying the temperature, humidity, concentrations of polymer and surfactant in the microemulsion method, we obtained the low dielectric constants of 2.24-2.81 and the low water absorptions of 0.49-0.59%, with decreases from 15.73% to 32.81% and 76.02% to 80.08%, respectively, as compared to thecase of the flat PI film; we also achieved the high tensile strengths of 97.7-103.2 MPa and high tensile moduli of 1.2-1.4 GPa, with the increases of 4.83-10.73% and 6.57-16.43%, respectively, as compared to the case of the flat PI film. Moreover, excellent durability of the low dielectric constant under high humidity condition was demonstrated by the very small increase in the dielectric constant (0.02-1%) in a moist environment. These results provide useful information for the structural design of high-performance dielectric materials.
Copyright © 2005 Polymer.cn All rights reserved
中国聚合物网 版权所有
经营性网站备案信息

京公网安备11010502032929号

工商备案公示信息

京ICP证050801号

京ICP备12003651号