PTFE conductive membrane for EVMD process and the application of electro-catalysis
来源:黄庆林教授/博导个人网站 发布日期:2017-07-18
作者:Liu, Huan Huang, Qinglin Wang, Yafeng Xiao, Changfa
关键字:PTFE conductive membrane EVMD Membrane fouling Electrochemical cleaning Electro-catalytic
论文来源:期刊
具体来源:Separation and Purification Technology
发表时间:2017年

To inhibit membrane fouling and to overcome the disadvantages of traditional conductive membranes,

polytetrafluoroethylene (PTFE) flat sheet membrane was used as the substrate to prepare a flexible conductive

membrane. Multi-walled carbon nanotubes (MWCNTs) and mixture of MWCNTs/graphene (mass

ratio 1:1) were employed as conductive layer. PTFE conductive membrane acted as a cathode which was

applied in EVMD (Electric vacuum membrane distillation) process to mitigate membrane fouling. The MD

flux increased from 4.97 to 8.89 L/m2 h which was because of not only electric field repulsion but also the

effect of electro-catalysis. MD flux recovered from 8.51 to 11.68 L/m2 h after electrochemical cleaning

(EC) for 4 h fixing electric field strength at 1.5 v/cm. Meanwhile PTFE conductive membrane was

employed in electro-catalytic degradation experiment, in which nano-TiO2 was used as the electrocatalyst.

In the electro-catalytic degradation experiment, the degradation rate of rhodamine red dye

was up to 99.25%, and composite membranes exhibited good electro-catalytic stability.