作者：J.Y. Dai, S.Q. Ma*, N. Teng, X.Y Dai, X.B. Shen, S. Wang, X.Q. Liu*, J. Zhu
关键字：2, 5-Furandicarboxylic acid, unsaturated polyester, bio-based polymers
论文来源：期刊
具体来源：Industrial & Engineering Chemistry Research
发表时间：2017年

A range of fully biobased unsaturated polyesters (bio-UPs) derived from 2,5-furandicarboxylic (FDCA),itaconic acid (IA), succinic acid (SA), and 1,3-propanediol (PD) were obtained via direct polycondensation. The chemical structures of the bio-UPs were identified by Fourier transfrom infrared spectroscopy and 1H NMR before they were cured together with a biobased, nonvolatile reactive diluent, guaiacol methacrylate (GM). The thermal and mechanical characterizations of the cured bio-UPs were evaluated using thermogravimetric analysis, 3-point bending tests, and dynamic mechanical analysis. Results showed that the thermal properties, flexural strength, and modulus of the cured bio-UPs were greatly improved after the introduction of FDCA. The temperature of 5% thermal weight loss reached 330 °C, and the flexural strength and modulus reached 122.8 and 3521 MPa, respectively. These results indicate that the bio-UPs have the potential to replace petroleum-based UPs.

全文链接：http://pubs.acs.org/doi/abs/10.1021/acs.iecr.7b00049