Polylactide/Cellulose Nanocrystal Composites: A Comparative Study on Cold and Melt Crystallization
来源:吴德峰教授个人网站 发布日期:2017-02-20
作者:Chunjiang Xu, Qiaolian Lv, Defeng Wu, Zhifeng Wang
关键字:cellulose nanocrystal; polylactide; composites; crystallization; nucleation.
论文来源:期刊
具体来源:Cellulose
发表时间:2017年

Cellulose, 2017, 24(5), 2163-2175.


ABSTRACT:

Polylactide (PLA) composites with pristine cellulose nanocrystals (CNC) and acetylated one (aCNC) were prepared for the crystallization study. The roles of CNC and aCNC in cold and melt crystallization of PLA were explored. Both CNC and aCNC have good nucleation activity during cold crystallization of PLA, but also highly impede transport of adjacent chain segments to the growing surface, acting as the role of physical barrier in the glassy bulk. Within the experimental temperature range, growth dominates the overall kinetics, rather than nucleation. Therefore, barrier role overwhelms nucleation agent one and as a result, the cold crystallization rates of composites decrease as compared with neat PLA, accompanied by decreased degrees of crystallinity. During melt crystallization, although the presence of CNC and aCNC leads to sharply increased system viscosities, reducing chain mobility, nucleation is the dominant role as the systems crystallize from the melts. Thus, the presence of CNC and aCNC promotes melt crystallization of PLA, and the composites show far higher crystallization rates and degrees of crystallinity than neat PLA. Besides, the surface acetylation of CNC improves its nucleation ability during melt crystallization of PLA, and as a result, the composite with aCNC has denser fold surfaces relative to the one with CNC. But the presence of these two kinds of particles has no evident influence on the lamellar structure of PLA whether in the cold or in melt crystallization. This work can provide useful information on the crystallization control of PLA using CNC.

PDF DOWNLOAD:

http://link.springer.com/article/10.1007/s10570-017-1233-x

Copyright © 2005 Polymer.cn All rights reserved
中国聚合物网 版权所有
经营性网站备案信息

京公网安备11010502032929号

工商备案公示信息

京ICP证050801号

京ICP备12003651号