Journal of Materials Science & Technology:通过构建阳离子-π相互作用改善石墨在生物降解淀粉材料中的分散和剥离:实现电磁屏蔽增强
来源:王明教授个人网站 发布日期:2022-09-03

论文摘要:Herein, a low-cost, biodegradable, and high-performance microwave shielding graphite/starch mate- rial was fabricated via constructing a cation- πinteraction between ammonium ions and graphite. The graphite flakes and starch were firstly mixed with distilled water containing ammonium hydroxide to form graphite/starch slurry under an ultrasonic assistant. The cation- πinteraction could improve delam- ination degree and dispersion of graphite in starch matrix. The slurry was first used as a coating material on the surface of wood and paper to develop shielding packages. The effect of coating thickness and coating layers on EM shielding property of the materials was investigated. Second, the composites with a high orientation of graphite were fabricated by compression at high pressures. The electrical conductivity and EM shielding effectiveness (SE T ) of the materials were greatly enhanced by construction of cation- πinteraction and orientation of graphite. Specifically, the EM SE T values increased from 56.9 to 66.8 dB for the composites with 50 wt.% graphite and 2.0 mm in thickness by constructing cation- πinteraction. The EM SE T values raised from 17.4 to 66.8 dB via the graphite orientation in the materials with the same components and thickness. The shielding mechanism of the compressed composites with orientation dispersion of graphite was also discussed in comparison to the coating layer with random dispersion of graphite.

全文链接:https://doi.org/10.1016/j.jmst.2022.04.045

Copyright © 2005 Polymer.cn All rights reserved
中国聚合物网 版权所有
经营性网站备案信息

京公网安备11010502032929号

工商备案公示信息

京ICP证050801号

京ICP备12003651号