祝贺课题组成员赵思培的文章发表于《Composites Part B: Engineering》
来源:王智教授个人网站 发布日期:2021-04-21

课题组成员赵思培文章发表于《Composites Part B: Engineering》,题目为:Curing mechanism, thermal and ablative properties of hexa-(4-amino-phenoxy) cyclotriphosphazene/benzoxazine blends

Abstract:

The demand for ablative material with high performance is eager in the aerospace industry. In this paper, hexa-(4-amino-phenoxy)-cyclotriphosphazene (CPA) was synthesized and then blended with bisphenol-A aniline benzoxazine (BA-a) firstly. The curing mechanism, thermal and ablative properties of cured blends were studied. The addition of CPA not only can decrease the curing temperature but can also increase the crosslink density of polybenzoxazine which is further beneficial for the improvement of thermal properties of cured blends. When the content of CPA is 5%, the Tg of the cured blend increases by 20 °C, and the char yield at 800 °C increases from 25.2% for pure polybenzoxazine to 49.2%. The oxyacetylene ablation tests showed that the ablation rate of cured blends could reach 0.047 mm s?1 while that of polybenzoxazine is 0.128 mm s?1. Further discussion based on SEM, XRD, Raman spectra showed that the CPA can effectively improve the graphitization degree of ablated samples and improve the integrity of graphite layer crystals. Moreover, the density functional theory (DFT) calculations and bond order analysis predict the bonding breakage sequence which is the C–N bonds between BA-a and CPA (N3–C55) > P–O bonds (P2–O12) > phosphazene ring, which means the phosphazene ring shows an effect after benzoxazine partly decomposed. The preparation method by adding CPA to benzoxazine to improve the ablative performance is facial and easy, which provides a new way of making novel ablative materials.

Copyright © 2005 Polymer.cn All rights reserved
中国聚合物网 版权所有
经营性网站备案信息

京公网安备11010502032929号

工商备案公示信息

京ICP证050801号

京ICP备12003651号